Lubricating oil additives, their preparation and use

ABSTRACT

A lubricating oil soluble compound suitable for use as a dispersant additive is obtainable by reacting at elevated temperature a polyacrylate with a dispersant having at least one reactive nitrogen--containing moiety. 
     Intermediates of the general formula IV ##STR1## where Y 1  is a group derived from the reaction of the polyacrylate with the reactive nitrogen-containing moieties (i.e. primary or secondary amine) are novel. 
     The process for preparing the lubricating oil soluble compounds can be a one step or multistep process. 
     Lubricating oil compositions comprise a major proportion of lubricating oil and a minor proportion of the lubricating oil soluble compounds.

This application is a continuation of application Ser. No. 07/674,617, filed on Mar. 25, 1991, now U.S. Pat. No. 5,186,853.

The present invention relates generally to novel lubricating oil soluble compounds suitable for use as dispersant additives in lubricating oils, their preparation and uses thereof.

Multigrade lubricating oils typically are characterized by two numbers such as 10W30, 5W30, and the like. The first number in the multigrade designation is associated with a maximum low temperature (e.g. 20° C.) viscosity requirement for that multigrade oil as measured typically by a cold cranking simulator (CCS) under high shear, while the second number in the multigrade designation is associated with a minimum high temperature (e.g. 100° C.) viscosity requirement. Thus, each particular multigrade oil must simultaneously meet both strict low and high temperature viscosity requirements in order to qualify for a given multigrade designation. Such requirements are set, for example, by ASTM specifications.

The minimum high temperature viscosity requirement is intended to prevent the oil from thinning out too much during engine operation thereby leading to excessive wear and increased oil consumption. The maximum low temperature viscosity requirement is intended to facilitate engine starting in cold weather and to ensure pumpability.

In formulating an oil which satisfactorily meets the extremes of viscosity requirements the formulator may use a single oil of desired viscosity or a blend of two lubricating oils of different viscosities at the same time as manipulating the nature and amounts of additives that must be present to achieve the overall target properties of a particular multigrade oil including its viscosity requirements.

In general, in order to meet the low and high temperature viscosity requirements of multigrade oils, it is necessary for the formulator to employ an additive conventionally referred to as a viscosity index (VI) improver. These generally function to increase the low temperature viscosity of the base oil to a lesser extent than they increase the high temperature viscosity. A complication for the formulator is the effect on the viscosity requirements posed by other lubricating oil additives, and in particular dispersants, which are added to prevent sludge flocculation and precipitation, the sludge being formed by oxidation of the oil. A problem with many existing dispersants is their low viscosities at higher temperatures.

The present invention seeks to overcome the problem associated with prior art dispersants by the provision of new lubricating oil soluble compounds suitable for use as dispersants having improved VI characteristics.

Accordingly, the present invention provides lubricating oil soluble compounds suitable for use as dispersant additives which compounds are obtainable by reacting at elevated temperature a polyacrylate with a dispersant having at least one reactive nitrogen--containing moiety.

Any dispersant having at least one reactive nitrogen--containing moiety may be employed. Thus dispersants having primary and/or secondary amino groups may be employed but not those containing exclusively tertiary amino groups. It is believed, though we do not wish to be bound by any specific theory, that reaction occurs between the reactive nitrogen--containing moiety of the dispersant and the olefinically unsaturated groups of the polyacrylate in a manner such that the dispersant is cross-linked by the polyacrylate molecules.

Suitable dispersants include (i) oil-soluble amides or imides of long chain hydrocarbyl-substituted mono- and dicarboxylic acids or their anhydrides, (ii) long chain hydrocarbons having a polyamine attached directly thereto, and (iii) Mannich condensation products formed by condensing a long chain hydrocarbyl-substituted hydroxy aromatic compound, for example an alkyl phenol, with an aldehyde and a polyalkene polyamine, which adduct contains at least one reactive amino group.

The dispersant is preferably an imide or amide formed by the reaction of a polyalkene substituted succinic acylating agent and an amine. Succinimides are a well-known class of dispersant useful in the process of the present invention. Typical of the art relating to such materials is GB-A-1565627 and the prior art acknowledged therein. Typically, they are prepared by reacting a polyalkene, in the presence or absence of chlorine, with either maleic acid, or preferably maleic anhydride, to produce a polyalkene-substituted succinic acid or anhydride and thereafter reacting the polyalkene-substituted succinic acid or anhydride with a nitrogenous material, suitably an amine, which may be a mono-, di- or polyamine.

A suitable succinimide has the formula: ##STR2## wherein R¹ is a hydrocarbyl group typically a polyolefin group. R¹ preferably contains between 30 and 300 carbon atoms, more preferably between 50 and 150. R² is a divalent group such that H₂ NR² NXY is an alkylene amine, such as an ethylene or propylene amine e.g. R² is -(CH₂ CH₂ NH₂)_(k) CH₂ CH₂ - where k is zero or an integer from 1 to 7 preferably 2 to 6, alternatively a mixed ethylene/propylene amine e.g. H₂ N(CH₂)₃ NH(CH₂)₂ NH(CH₂)₃ NH₂ can be used.

X and Y are independently either hydrogen, alkyl or hydroxyalkyl each preferably of 1-6 carbons especially methyl ethyl or hydroxy ethyl, or together form the group: ##STR3##

Alternatively, R² in the formula (I) may be a divalent group such that H₂ NR² NXY is an alkanolamine or a polyetheramine. Typically such alkanolamines may contain the group =N.CH₂ CH₂ NH.CH₂ CH₂ OH (i.e. R² =CH₂ CH₂, X=H, Y=CH₂ CH₂ OH) and such polyetheramines may contain the group =N.CH₂ CH₂ OCH₂ CH₂ OCH₂ CH₂ NH₂ (i.e. R² =(CH₂ CH₂ O)₂ CH₂ CH₂, X=Y=H). Useful commercially available polyetheramines are the Jeffamines (RTM) marketed by Texaco. R² is preferably an alkylene group e.g. of 2 to 40 carbons, optionally interrupted with at least one O or NH group, and in particular contains one or more units of alkylene oxa or alkylene amino groups, each of 2-4 carbons.

R² may also be a divalent group such that H₂ NR² NXY is an aromatic or araliphatic amine e.g. of 6-20 carbons such as phenylene or biphenylene diamine or bis (amino benzyl).

Where one of X and Y is hydrogen, R² may be an alkylene group e.g. -CH₂ CH₂ -. It is preferred that the dispersant used in the present invention contains at least 2 active nitrogens (i.e. primary or secondary) more preferably from 3 to 7.

Suitably in the formulae (I) and (II) R¹ is derived from either ethylene, propylene, 1-butene, isobutene, 1-hexene, 1-octene and the like. Alternatively, the polyalkene may be derived from an internal olefin, e.g. 2-butene, or an interpolymer, e.g. an ethylene/propylene copolymer. Preferably the polyalkene is a polyisobutene.

The succinimide may be either a mono- or bis-succinimide.

Polyacrylates are defined as compounds comprising at least two unsaturated acrylic groups. For the purpose of this invention the terms "polyacrylates" and "polyacrylamides" include and alpha substituted derivatives of acrylate and acrylamide groups.

Polyacrylates and polyacrylamides (when Z¹ or Z² is =NR⁶) useful in the present invention may suitably be those having the formula: ##STR4## wherein R³ is either alkylene, arylene, alkylene glycol, or alkylene acrylate (or its amine derivative), R⁴ and R⁵ are independently either hydrogen or a hydrocathy1 moiety, and Z¹ and Z² are independently a heteroatom, or a substituted heteroatom for example -O- or =NR⁶ where R⁶ is hydrogen or an alkyl group e.g. methyl or ethyl.

In formula III where R₃ is alkylene e.g. of 1-300 or 1-10 carbons, it is suitably of the formula -[CHR⁷ ]_(n) - where R⁷ is hydrogen or a C₁ -C₂₀ preferably C₁ -C₁₀, more preferably C₁ -C₆ alkyl group more preferably methyl or ethyl; n is an integer from 1 to 30; each of the n -[CHR⁷ ]- groups can be the same or different. The group R³ is suitably derived from a polyolefin for example where R⁷ is hydrogen, R³ will typically be derived from polyethylene.

Where R³ is an alkylene glycol, it is suitably of the formula -[CHR⁸ CHR⁹ O]_(m) CHR⁸ CHR⁹ - where R⁸ and R⁹ are independently H, or a C₁ -C₂₅ preferably C₁ -C₁₆ more preferably C₁ -C₆ alkyl group for example methyl or ethyl and m is an integer from 1 to 10. Preferably R⁸ is hydrogen and R⁹ is hydrogen, methyl or ethyl. Where R⁹ is hydrogen, methyl or ethyl the alkylene glycol will usually be derived from ethylene, propylene or butylene oxides respectively. Each of the -[CHR⁸ CHR⁹ O]- groups can be the same or different. HZ¹ R³ Z² H is preferably a polyalkylene glycol.

R₃ may also be an arylene aralkylene or alkarylene group e.g. of 6-20 or 7-20 carbons such as phenylene, naphthylene benzylene -CH₂ Ph- biphenylene -Ph-Ph- or methylene diphenylene -PhCH₂ Ph- or -PhCMe₂ Ph-.

Alternatively R₃ may be an alkylene acrylate group comprising acrylate or acrylamide groups e.g. R³ =-[CAB]_(p) - where each of A and B is independently the group ##STR5## and p is an integer from 1 to 10 e.g. 3-5, and q is zero or an integer from 1 to 5, (this group preferably representing group A in at least one part of R³) or is hydrogen, R⁷, a hydroxy alkyl group e.g. of 1-6 carbons; each of the p groups -[CAB]- may be the same or different, R⁴, Z¹ R⁷ are all as defined above, and the alkylene group preferably has 1-6 carbons.

Preferably alkylene in the group A is methylene; when B is a hydroxy alkyl group it is preferably hydroxy ethyl.

R³ is preferably an alkylene, alkylene glycol or alkylene acrylate (as defined above), especially in the form --CHR⁷ -CAB--CHR⁷ -.

Where R⁴ or R⁵ is a hydrocarbyl moiety it is preferably a C₁ -C₆ alkyl group.

R⁴ and R⁵ are preferably hydrogen or methyl.

Examples of suitable polyacrylates having the formula (III) include ethyleneglycol dimethacrylate (H₂ C=CMeCO₂ -(CH₂)2-O2CMeC=CH₂) butanediol dimethacrylate (H₂ C=CMeCO₂ -(CH₂)₄ -O₂ CMeC--CH₂), triethyleneglycol dimethacrylate, (H₂ C=CMeCO₂ -(CH₂ CH₂ O)₃ -OCMeC=CH₂), 4,4'- isopropylidene-diphenol dimethacrylate (H₂ C=CMeCO₂ -C₆ H₄ -C(Me)₂ -C₆ H₄ -O₂ CMeC=CH₂), hexanediol diacrylate (H₂ C=CHCO₂ -(CH₂)₆ -O₂ CHC=CH₂, diethylene glycol diacrylate (H₂ C=CHCO₂ -(CH₂ CH₂ O)₂ -OCHC=CH₂), tripropylene glycol diacrylate (H₂ C--CHCO₂ -(C₃ H₆ O)₃ -OCHC=CH₂), pentaerythritol triacrylate (H₂ C=CHCO₂ CH₂)₃ CCH₂ OH), pentaerythritol tetraacrylate (H₂ C=CHCO₂ CH₂)₃ C(CH₂ O₂ CCH=CH₂) and N,N'-methylene bisacrylamide (H₂ C=CHCO-NHCH₂ NH-OCCH=CH₂).

The dispersant having the formula (II) may be reacted with the polyacrylate having the formula (III) in a single step or in two or more sequential steps. Thus, the reaction of the dispersant with the polyacrylate may suitably comprise in a first step reacting dispersant at elevated temperature with polyacrylate, and in a further step or steps reacting the product from the preceding step or steps with further dispersant.

It will be appreciated that in the subsequent sequential step or step involving the addition of further dispersant, a different dispersant or dispersants to that used in the first step may be employed.

It is preferred to effect the reaction in a suitable solvent. In view of the fact that dispersants are generally marketed as solutions in lubricating oils and in view of the intended use of the product, it is preferred to employ a lubricating oil as the solvent. Both natural and synthetic lubricating oils may be employed. Cosolvents may also be used if desired. Suitable cosolvents include liquid hydrocarbons, for example xylene and toluene.

The elevated temperature at which the reaction is effected may be above 70° C. and below the decomposition temperature of any of the components of the reaction mixture.

A single step process may suitably comprise adding over a period, for example from 5 to 180 minutes, the polyacrylate to a solution of the dispersant at a temperature of from 75° to 220° C. and thereafter reacting the mixture at a temperature above 70° C. and below the decomposition temperature of the mixture for a period sufficient to effect reaction, for example from 30 to 300 minutes, at either atmospheric or subatmospheric pressure. The polyacrylate may suitably be pre-heated if desired to a temperature below its decomposition temperature.

A two step process may suitably comprise (i) mixing the dispersant and the polyacrylate at a temperature of from ambient to 120° C. (ii) in the event that the temperature of the mixture is less than 70° C., raising its temperature to a value above 70° C. and below the decomposition temperature of the mixture over a period, for example from 10 to 180 minutes, (iii) maintaining the mixture at this temperature for a period, for example from 15 to 300 minutes, (iv) adding a further portion of a dispersant, suitably preheated to a temperature up to 220° C., and (v) maintaining the temperature of the mixture at a value in the range from 70° to 250° C. for a period, suitably from 15 to 300 minutes, at either atmospheric or subatmospheric pressure.

In one step at least I equivalent e.g. 1 -10 equivalents of NH group in the dispersant may be reacted per equivalent of polyacrylate.

In the aforesaid two step (or multistep) reaction 0.75 or more, preferably 0.85 to 1.1 equivalents of polyacrylate may be used in the first step for each amino hydrogen present in the dispersant. Thereafter in the subsequent step or steps, from 0.5-15 preferably 1-10 equivalents of dispersant per equivalent of dispersant used in the first step are used.

The process may be operated batchwise or continuously.

Products of the first step of a 2-step or multistep reaction of a dispersant as described hereinabove and a polyacrylate of formula III comprise a novel compound of the general formula IV: ##STR6## where R¹¹ and R¹² are independently a divalent aliphatic, hereto-substituted aliphatic, aromatic or hetero-substituted aromatic group, e.g. as defined for R² and with any aromatic groups containing 6-20 carbons such as phenylene. R¹⁰ and R¹³ are independently a hydrocarbyl group, or ##STR7##

Y¹ is -CH₂ CR⁴ (CO)Z¹ R³ Z² (CO)CR⁵ =CH₂

R¹⁴, R¹⁵ and R¹⁶ are independently a hydrocarbyl or substituted hydrocarbyl group;

R¹⁷ is an aliphatic or hereto (e.g. O) substituted aliphatic group, e.g. as defined for R²

x and y are independently zero or an integer from 1 to 10,

each R¹¹ each R¹² and each Y¹ can be the same or different,

R³, R⁴, R⁵, Z¹ and Z² are as defined above.

Where R¹⁰, R¹³, R¹⁴, R¹⁵ or R¹⁶ is a hydrocarbyl group e.g. of 1-300 carbons, it is preferably derived from a polyolefin which is derived from a C₁ -C₈ terminal or internal olefin e.g. polyethylene, polypropylene or polyisobutene preferably polyisobutene. Preferably it is a C₃₀ -C₃₀₀ alkyl group more preferably C₅₀ -C₁₅₀.

R¹⁷ is suitably ethylene or propylene.

The reactions are performed in the absence of any catalyst which is active in the polymerisation of polyacrylates. By the avoidance of such catalysts the production of polymerised polyacrylates can be substantially avoided.

In another aspect the present invention provides a finished lubricating oil composition which composition comprises a major proportion of a lubricating oil and a minor proportion of the dispersant additive of the invention or the compound of formula IV as hereinbefore described.

The lubricating oil may be any natural or synthetic lubricating oil.

Into the lubricating oil composition there may also be incorporated any of the conventional additives normally employed, which additives include antioxidants, detergents, extreme pressure/anti-wear agents and viscosity index improvers. It is an advantage of the present invention that, because the dispersant composition of the invention has viscosity index properties, less of the conventional viscosity index improver may be required.

The lubricating oil composition may be used for any lubricating application, including automotive and marine use.

For automotive use the lubricating oil composition may suitably contain up to 10% by weight (e.g. of 0.01-10% or 2-10% of the dispersant additive of the present invention.

For marine engine use the lubricating oil composition may suitably contain up to 10% by weight (e.g. 0.0-10% or 2-10%) of the dispersant additive of the present invention.

The invention will now be illustrated by reference to the following Examples.

In all the Examples there was used a commercially available succinimide dispersant formed by the reaction of a polyisobutene (M_(n) about 1000) --substituted succinic anhydride and tetraethylene pentamine.

In the Table reference is made to LZ 6420, which is a dispersant having VI credit marketed by Lubrizol. It is used for comparison purposes.

ONE STEP ROUTE EXAMPLE 1

A 50% solution of the succinimide dispersant in SN150 oil was heated to 120° C. Pentaerythritol triacrylate (PETA)(0.65, 0.82 or 1.07 molar equivalents) was added to the dispersant solution in a single addition. The resulting mixture was heated at 120°-30° C. for 180 minutes at atmospheric pressure and for 60 minutes at reduced pressure (60mm Hg).

The viscosities were recorded on solutions of 11.0% (by weight) of products

SEQUENTIAL TWO STEP ROUTE EXAMPLE 2

The succinimide dispersant was combined with four equivalents of 6-hexanediol diacrylate (HDODA) at ambient temperature. The mixture was heated to 120° C. over 30 minutes and maintained at this temperature for 60 minutes. A further one or two equivalents of the succinimide dispersant at a temperature of 75° C. were added to the mixture. The mixture was then heated at 120° C. for 120 minutes at atmospheric pressure and for 60 minutes at reduced pressure (60mm Hg).

The viscosities were recorded as 11.0% (b.w. of products) solutions in SN150 oil at -20, 40 and 100° C. and are given in the accompanying Table.

EXAMPLE 3

The succinimide dispersant was combined with four equivalents of tripropyleneglycol diacrylate (TRPGDA) at ambient temperature. The mixture was heated to 120° C. over 35 minutes and maintained at this temperature for 60 minutes. A further one or two equivalents of the succinimide dispersant at a temperature of 70° C. were added to the mixture. The resultant mixture was heated to 120° C. for 210 minutes at atmospheric pressure.

The viscosities were recorded as 11.0% or 12.0% (b.w of products) solutions in SN150 oil at -20, 40 and 100° C. and are given in the accompanying Table.

EXAMPLE 4

The succinimide dispersant was combined with four equivalents of N,N'-methylenebisacrylamide (MBA) at 21° C. The mixture was heated to 145° C. over 50 minutes and maintained at this temperature for 40 minutes. A further two equivalents of the succinimide dispersant at a temperature of 90° C. were added to the mixture. The resultant mixture was heated to 135° C. for 210 minutes at atmospheric pressure.

The viscosities were recorded as 13% oil (b.w) solutions at -20, 40 and 100° C. and are given in the accompanying Table.

                                      TABLE                                        __________________________________________________________________________                 Concn.                                                                              Concn.                                                                    of   of   VISCOSITY                                                            products                                                                            actives                                                                             -20° C.                                                                     40° C.                                                                      100° C.                                                                     Viscosity                                    Example     (% b.w)                                                                             (% b.w)                                                                             Poise                                                                              c/s c/s Index                                        __________________________________________________________________________          LZ6420 11.0 5.5  38.00                                                                              53.2                                                                               8.38                                                                               131                                               Succinimide                                                                           11.0 5.5  35.75                                                                              43.2                                                                               6.76                                                                               108                                          1    Succinimide:                                                                   PETA                                                                           1:1.07 11.0 6.2  --  82.1                                                                               12.90                                                                              157                                               1:0.82 11.0 6.1  --  50.4                                                                               8.18                                                                               135                                               1:0.65 12.0 6.5  34.2                                                                               44.7                                                                               7.37                                                                               130                                          2    Succinimide:                                                                   HDODA:                                                                         Succinimide                                                                    1:4:1  11.0 6.4  27.9                                                                               57.9                                                                               9.90                                                                               158                                               1:4:2  11.0 6.1  32.6                                                                               44.9                                                                               7.42                                                                               129                                                      13.0 7.2  37.9                                                                               51.0                                                                               8.24                                                                               133                                          3    Succinimide:                                                                   TRPGDA:                                                                        Succinimide                                                                    1:4:1  11.0 6.7  32.7                                                                               51.8                                                                               9.18                                                                               161                                               1:4:2  12.0 6.9  35.3                                                                               51.1                                                                               8.50                                                                               142                                          4    Succinimide:                                                                          13.0 7.0  --  46.5                                                                               7.40                                                                               122                                               MBA:                                                                           Succinimide                                                                    1:4:2                                                                     __________________________________________________________________________      *`Actives` refers to any material that is not mineral oil, ie amount of        succinimide + polyacrylate present by weight.                                  **` Conc. of product` refers to % weight of end material (which contains       oil already) diluted in oil.                                             

With reference to the Table it can be seen that by using the dispersants according to the present invention increased viscosities can be achieved at high temperatures without any significant low temperature viscosity penalties, and often the low temperature viscosity is lower in the product (polyacrylate treated dispersant) relative to the conventional material. 

I claim:
 1. An oil soluble compound suitable for use as a dispersant additive which compound is obtainable by reacting at elevated temperature a dispersant which is a long chain hydrocarbon having a polyamine attached directly thereto with either a polyacrylate or a polyacrylamide having the formula (III): ##STR8## wherein R³ is alkylene, arylene glycol, or alkylene acrylate, R⁴ and R⁵ are independently either hydrogen or a hydrocarbyl moiety, and Z¹ and Z² are independently either -O- or =NR⁶, where R⁶ is hydrogen, methyl or ethyl.
 2. An oil-soluble compound as claimed in claim 1 wherein the dispersant contains between 3 and 7 active nitrogens.
 3. An oil-soluble compound as claimed in claim 1 wherein R³ is an alkylene group of formula -[CHR⁷ ]_(n) - where R⁷ is hydrogen or a C₁ -C₆ alkyl group and each of the n -[CHR⁷ ]- groups can be the same or different and n is an integer of from 1 to
 30. 4. An oil-soluble compound as claimed in claim 1 wherein R³ is an alkylene glycol of the formula:

    -[CHR.sup.8 CHR.sup.9 O].sub.m CHR.sup.8 CHR.sup.9 -

wherein R⁸ and R⁹ are independently hydrogen or a C₁ -C₆ alkyl group, and m is an integer from 1 to 10, each of the -[CHR⁸ CHR⁹ O]- groups can be the same or different. 